Product Data Sheet Show all documents

Sikacrete®-114

FREE FLOWING MICRO-CONCRETE FOR GROUTING AND REPAIR

Sikacrete®-114 is a one component, free-flowing, high strength, non-shrink, cement based micro-concrete with a maximum aggregate size of 10 millimeter.
Suitable for use in hot and tropical climatic conditions.

One component, requires the addition of water only
  • Reduced waste and risk of mixing failures
  • Easy to mix, apply and finish
  • Economical
  • Excellent adhesion
  • Shrinkage compensated
  • Rapid strength development
  • Compatible with the properties of typical concrete
  • Vapour permeable
Find a Store
Product Data Sheet Show all documents

Usage

Sikacrete®-114 is used for the structural repair of deteriorated concrete.
It is ideal for casting sections or members where the volumes required are too large for conventional grouts, and too small and inaccessible for normal concreting applications.
A typical application is the re-profiling of damaged concrete members, using formwork.
Also suitable for base plate grouting where thickness exceeds 100 millimetre.  

Advantages

One component, requires the addition of water only
  • Reduced waste and risk of mixing failures
  • Easy to mix, apply and finish
  • Economical
  • Excellent adhesion
  • Shrinkage compensated
  • Rapid strength development
  • Compatible with the properties of typical concrete
  • Vapour permeable

Packaging

40 kg bag

Colour

Grey powder

Product Details

Product Information

Chemical Base

Portland cement, selected fillers and aggregates, special additives

Shelf Life

12 months minimum from date of production

Storage Conditions

Store in original unopened packaging in cool and dry condition between 5 °C and 35 °C. Protect from direct sunlight, heat and moisture.

Density

~2.4 kg/l (25 °C) (fresh mortar)

Maximum Grain Size

Max. 10 mm
Technical Information

Compressive Strength

1 Day

7 Day

28 Day

4.2 L water / 40 kg at 25 °C≥  35 N/mm2≥  45 N/mm2≥  65 N/mm2

Modulus of Elasticity in Compression

≥  33 000 N/mm2(ASTM C 469-94)

Tensile Strength

~5 N/mm2

(ASTM C307)

Tensile Adhesion Strength

>  1.5 N/mm2 (concrete failure)(BS 1881)

Water Absorption

~2.3 % (28 d)(BS 1881)

Application

Application Information

Mixing Ratio

4.0 - 4.25 L of water per 40 kg bag

Layer Thickness

Min. 50 mm per pour
Max. 500 mm per pour		(Min. 100 mm for baseplate grouting)

Ambient Air Temperature

+5 °C min. / +35 °C max.

Substrate Temperature

+5 °C min. / +35 °C max.

Pot Life

~2 h (25 °C)
Consumption

Yield

~18.4 L / 40 kg bag
Application steps

MIXING

Always empty the full contents of the bag into a suitable mixer.
Mix dry for 3 minutes before adding the water.
Add 4.0 to 4.25 litre of water per 40 kilogram bag.
Best mixed in a forced action mixer.
Do not mix by hand or mix part bags!
For best results, first add 3.5 to 3.8 litre of water and mix for at least 3 minutes or until the larger aggregate has thoroughly dispersed and a uniform, free flowing consistency is obtained. Then add remaining water and mix for additional 2 minutes.

APPLICATION

Dampen all concrete surfaces thoroughly with clean water prior to application.
Before pouring, however, let the mixed grout stand for 2 to 3 minutes after mixing with the mixing water to allow entrapped air to escape.
Maintain sufficient hydrostatic head to keep the product flowing.
Provide channels for the air to escape during grouting.
Protect from rain until initial set has been achieved.

CURING TREATMENT

Treat exposed surfaces with Antisol-WB curing compound or use other approved curing methods such as polyethylene sheeting or wet hessian.
Do not commence fogging until final set has been reached.

CLEANING OF TOOLS

Clean equipment and mixer after application with water.
Hardened material can only be removed mechanically.