Sikaflex® AT Connection
Universal STP construction sealant for connection joints
Sikaflex® AT Connection is an isocyanate free, silane terminated polymer sealant. It provides a waterproof, elastic seal with good mechanical properties over a wide range of temperatures.
- Moisture curing
- Isocyanate free
- Waterproof
- Good mechanical properties
- Resistant to weathering
- Good adhesion to porous and non-porous construction materials
- Elastic over a wide range of temperatures
- Movement capability ±25 % (ISO 9047)
- 1-part
- Low VOC emissions
- Primerless for most substrates
Usage
Sealing joints for:- Movement and connection joints
- Facade elements
- Balconies
- Window and door frames
- Pre-cast elements
- Infill panels
- Cladding
- Curtain walling
- Interior and exterior use
Advantages
- Moisture curing
- Isocyanate free
- Waterproof
- Good mechanical properties
- Resistant to weathering
- Good adhesion to porous and non-porous construction materials
- Elastic over a wide range of temperatures
- Movement capability ±25 % (ISO 9047)
- 1-part
- Low VOC emissions
- Primerless for most substrates
Packaging
300 ml cartridges | 12 cartridges per box |
600 ml foil pack | 20 foil packs per box |
Refer to current price list for packaging variations
Colour
Colour range to be defined by local sales organisation.
Product Details
ENVIRONMENTAL INFORMATION
- Conformity with LEED v4 EQc 2: Low-Emitting Materials
- VOC emission classification GEV-Emicode EC1PLUS, license number 1830/20.10.00
APPROVALS / STANDARDS
- CE Marking and Declaration of Performance to EN 15651-1 - Sealants for non-structural use in joints in buildings - Facade elements - F-EXT-INT CC
- CE Marking and Declaration of Performance to European Technical Assessment ETA 17/0980, based on EAD 350141-00-1106 - Fire stopping and fire sealing products, linear joint and gap seals
- ISO 11600-F Class 25HM, Sikaflex AT-Connection, SKZ, Report, No 102557/12-II
- Cleanroom Suitability Sikafloor®, Fraunhofer IPA, Report No. SI 1008-533
Chemical Base
Silane terminated polymer
Shelf Life
12 months from date of production
Storage Conditions
The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +25 °C. Always refer to packaging.
Density
~1,30 kg/l | (ISO 1183-1) |
Product Declaration
EN 15651-1: F EXT-INT CC
ISO 11600: F Class 25HM
Shore A Hardness
~24 (after 28 days) | (ISO 868) |
Secant Tensile Modulus
~0,40 N/mm2 at 100 % elongation (23 °C) | (ISO 8339) |
~0,60 N/mm2 at 100 % elongation (−20 °C) |
Elastic Recovery
~70 % | (ISO 37) |
Tear Propagation Resistance
~4,5 N/mm | (ISO 34) |
Movement Capability
± 25 % | (ISO 9047) |
Resistance to Weathering
8 | (ISO / DIS 19862) |
Service Temperature
−40 °C to +70 °C
Joint Design
The joint dimensions must be designed to suit the movement capability of the sealant. The joint width must be a minimum of 10 mm and a maximum of 35 mm. A width to depth ratio of 2:1 must be maintained (for exceptions, see table below).
Typical joint dimensions for joints between concrete elements:
Joint distance [m] | Min. joint width [mm] | Min. joint depth [mm] |
2 | 10 | 10 |
4 | 15 | 10 |
6 | 20 | 10 |
8 | 30 | 15 |
10 | 35 | 17 |
All joints must be correctly designed and dimensioned in accordance with the relevant standards and codes of practice before their construction. The basis for calculation of the necessary joint widths are the type of structure, dimensions, technical values of the adjacent building materials, joint sealing material and the specific exposure of the building and the joints.
For larger joints, contact Sika Technical Services for additional information.
Application
Backing Material
Use closed cell, polyethylene foam backing rods
Sag Flow
0 mm (20 mm profile, +50 °C) | (ISO 7390) |
Ambient Air Temperature
+5 °C to +40 °C
Substrate Temperature
+5 °C to +40 °C, min. +3 °C above dew point temperature
Curing Rate
~2 mm/24 hours (+23 °C / 50 % r.h.) | (CQP* 049-2) |
* Sika Corporate Quality Procedure
Skin Time
~60 minutes (23 °C / 50 % r.h.) | (CQP 019-1) |
Tooling Time
~45 minutes (+23 °C / 50 % r.h.) | (CQP 019-2) |
Consumption
Joint width [mm] | Joint depth [mm] | Joint length [m] per 600 ml foil pack |
10 | 10 | 6 |
15 | 10 | 4 |
20 | 10 | 3 |
25 | 12 | 2 |
30 | 15 | 1,3 |
Consumption depends on the roughness and absorbency of the substrate.
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
SUBSTRATE PREPARATION
The substrate must be sound, clean, dry and free of all contaminants such as dirt, oil, grease, cement laitance, old sealants and poorly bonded paint coatings which could affect adhesion of the sealant. The substrate must be of sufficient strength to resist the stresses induced by the sealant during movement.
Removal techniques such as wire brushing, grinding, grit blasting or other suitable mechanical tools can be used.
All dust, loose and friable material must be completely removed from all surfaces before application of any activators, primers or sealant.
Sikaflex® AT Connection adheres without primers and/or activators.
For optimum adhesion, joint durability and critical, high performance applications such as joints on multi-storey buildings, highly stressed joints, extreme weather and / or water exposure. The following priming and/or pre-treatment procedures must be followed:
Non-porous substrates
Aluminium, anodised aluminium, stainless steel, PVC, galvanised steel, powder coated metals or glazed tiles. Slightly roughen surface with a fine abrasive pad. Clean and pre-treat using Sika® Aktivator-205 applied with a clean cloth.
Before sealing, allow a waiting time of > 15 minutes (< 6 hours).
Other metals, such as copper, brass and titanium-zinc, cleaned and pre-treat using Sika® Aktivator-205 applied with a clean cloth. After a waiting time of > 15 minutes (< 6 hours). Apply Sika® Primer-3 N applied by brush. Before sealing, allow a waiting time of > 30 minutes (< 8 hours)
PVC has to be cleaned and pre-treated using Sika® Primer-215 applied with a brush. Before sealing, allow a waiting time of > 30 minutes (< 8 hours).
Glass must be cleaned with Isopropanol before application
Porous substrates
Porous substrates must be primed using Sika® Primer-3 N applied by brush. For more details such as application and flash-off times, refer to the most recent Product Data Sheet of the respective pre-treatment product.
Before sealing, allow a waiting time of > 30 minutes (< 8 hours).
Adhesion tests on project specific substrates must be performed and procedures agreed with all parties before full project application.
For more detailed advice and instructions contact Sika Technical Services.
Note: Primers and activators are adhesion promoters and not an alternative to improve poor preparation / cleaning of the joint surface. Primers also improve the long term adhesion performance of the sealed joint.
MIXING
1-part ready to use
CLEANING OF TOOLS
Clean all tools and application equipment immediately after use with Sika® Remover-208. Hardened material can only be removed mechanically. For cleaning skin, use Sika® Cleaning Wipes-100.